Starex TF-0930
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgZ0Zf_Starex-TF-0930.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex TF-0930 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20 mm | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 3.20 mm | 0.60 | % | ASTM D955 |
| Flow : 3.20 mm | 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 | |
| Pencil Hardness 1 | 2H | JIS K5401 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 3 | 61.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/5 |
| Break 4 | 52.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 5 | 12 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 6 | 2800 | MPa | ASTM D790 |
| -- 7 | 2600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 93.0 | MPa | ASTM D790 |
| -- 9 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10 | ISO 179/1eA | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 20 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 20 | J/m | ASTM D256 |
| -30°C 11 | 30 | kJ/m² | ISO 180/1A |
| 23°C 12 | 2.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 290 | J/m | |
| 23°C, 6.35 mm | 290 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 103 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 84.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 to 3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | Condition: 500g |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 5.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.8 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | Thickness: 4 mm |
| 11 . | Thickness: 4 mm |
| 12 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4003 A FR | RTP Company | PPA | RTP |
| POWERSIL® 735 A/B LIGHT GRAY | Wacker Chemie AG | Silicone | POWERSIL® |
| RTP 100 SI 2 | RTP Company | PP, Unspecified | RTP |
| Teldene® B20ML | National Petrochemical Industries Company (NATPET) | PP Impact Copolymer | Teldene® |
| VITAMIDE® AR37BK8524 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |