Order Products : sales@su-jiao.com
AT 191A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgEv9l_AT-191A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is suitable for use in hot melt adhesive and coating applications. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.913 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 125°C/0.325 kg | 160 | g/10 min | |
| 190°C/2.16 kg | 160 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 7.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 120 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 125 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 100 | °C | DSC |
| Ring and Ball Softening Point | 115 | °C | ASTM E28 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 450Y-X10 | Toray Resin Company | ABS | Toyolac® |
| TOTAL Polyethylene HDPE 8183 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| KPOL-NYLON K-NY6/27B | KPOL Chem Co. | Nylon 6 | KPOL-NYLON |
| Iupilon® EHG2010R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Petrothene® Select GS906061 | LyondellBasell Industries | LLDPE | Petrothene® Select |