Amilan® CM1003G30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DgBnxS_Amilan-CM1003G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM1003G30 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.50 to 0.80 | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.40 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | |
| Saturation, 23°C | 6.4 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 160 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles) | 24.0 | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.200 | Suzuki Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 224 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Melting Temperature | 225 | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5017 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Calsak ABS CS-72L | Calsak Polymers | ABS | Calsak ABS |
| CERTENE™ PHF-4 | Muehlstein | PP, HMS | CERTENE™ |
| Fainplast PVC PH 70/AS | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| LNP™ THERMOCOMP™ D251 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |