| General Information | |
|---|
| Additive | - Antiblock (2500 ppm)
- Processing Aid
- Processing Stabilizer
- Slip (1000 ppm)
|
| Features | - Antiblocking
- Food Contact Acceptable
- Good Processability
- Good Tear Strength
- Good Toughness
- Low Density
- Low Gel
- Slip
|
| Uses | |
| Agency Ratings | - FDA 21 CFR 176.170(c), Table 2, Cond. B
- FDA 21 CFR 176.170(c), Table 2, Cond. C
- FDA 21 CFR 176.170(c), Table 2, Cond. D
- FDA 21 CFR 176.170(c), Table 2, Cond. E
- FDA 21 CFR 176.170(c), Table 2, Cond. F
- FDA 21 CFR 176.170(c), Table 2, Cond. G
- FDA 21 CFR 176.170(c), Table 2, Cond. H
- FDA 21 CFR 177.1520(c) 3.2a
|
| Processing Method | - Coextrusion
- Film Extrusion
|
| Films | Nominal Value | Unit | Test Method |
|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | | | ASTM D882 |
| 1% Secant, MD
: 25 µm, Blown Film | 135 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 145 | MPa | |
| Tensile Strength | | | ASTM D882 |
| MD
: Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD
: Yield, 25 µm, Blown Film | 9.00 | MPa | |
| MD
: Break, 25 µm, Blown Film | 43.0 | MPa | |
| TD
: Break, 25 µm, Blown Film | 34.0 | MPa | |
| Tensile Elongation | | | ASTM D882 |
| MD
: Break, 25 µm, Blown Film | 550 | % | |
| TD
: Break, 25 µm, Blown Film | 730 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 800 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm, Blown Film | 320 | g | |
| TD
: 25 µm, Blown Film | 480 | g | |
| Seal Initiation Temperature 1(25 µm, Blown Film) | 100 | °C | |