InnoTooling™ IE-9070
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTooling™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Df5zSz_InnoTooling-IE-9070.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-9070 is a slow reacting polyurethane formulated for room temperature hand mix dispensing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or TDI. This product is especially developed for translucent mass castings. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.07 | g/cm³ | |
| Hardener | 1.07 | g/cm³ | |
| Base Resin | 1.07 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 20 Mix Ratio by Weight: 20 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 480 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.19 | Pa·s | |
| 25°C 2 | 2.4 | Pa·s | |
| 25°C 3 | 6.5 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 15 to 25 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 65 to 75 | ASTM D2240 | |
| Tensile Strength | 5.52 | MPa | ASTM D638 |
| Tensile Elongation at Break | 300 | % | ASTM D638 |
| Tear Strength | 17.5 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYNIL® P50 FLBK | Nilit Plastics | Nylon 66 | POLYNIL® |
| Tenac™ LS701 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Anjacom® 250-H/GF30 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Hylon® N2200STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| Karina BLACK PVC COMPOUND -E 48/ 23-RG-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |