Sarlink® TPV 4155N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DebPeC_Sarlink-TPV-4155N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® 4155N is a low hardness grade possessing exceptional tensile strength, superior compression set, chemical resistance and high temperature performance. It can be easily processed by injection molding, blow molding or extrusion for various applications such as boots and bellows, seals, gaskets as well as other profiles and articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.958 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 53 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 56 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Transverse flow : 100% strain | 2.00 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 3.10 | MPa | ISO 37, ASTM D412 |
| Tensile Stress | |||
| Transverse flow : Fracture | 5.20 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 4.30 | MPa | ISO 37, ASTM D412 |
| Tensile Elongation | |||
| Transverse flow : Fracture | 550 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 240 | % | ISO 37, ASTM D412 |
| Tear Strength - Across Flow | |||
| -- | 22 | kN/m | ASTM D624 |
| -- 1 | 22 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 14 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 26 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 37 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -5.0 | % | ASTM D573, ISO 188 |
| 100% strain 135°C, 1000 hr | 2.0 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -9.0 | % | ASTM D573, ISO 188 |
| 100% strain 150°C, 168 hr | -2.0 | % | ASTM D573, ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow | |||
| 135°C, 1000 hr | 1.0 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -6.0 | % | ISO 188, ASTM D573 |
| Change in Shore Hardness in Air | ASTM D573, ISO 188 | ||
| Support a, 135°C, 1000 hr | 2.0 | ASTM D573, ISO 188 | |
| Support a, 150°C, 168 hr | 2.0 | ASTM D573, ISO 188 | |
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 85 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 320 | Pa·s | ASTM D3835 |
| 200°C | 320 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 215 | °C | |
| Middle Temperature | 180 - 215 | °C | |
| Front Temperature | 180 - 215 | °C | |
| Nozzle Temperature | 187 - 220 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 205 | °C | |
| Cylinder Zone 3 Temp. | 187 - 210 | °C | |
| Cylinder Zone 4 Temp. | 187 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C | |
| Die Temperature | 195 - 215 | °C | |
| Take-Off Roll | 20.0 - 50.0 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: general purposeCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® U4830HSL BK01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Xuchuan XCS-3100HE | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Next PPS PPSG40-02NC | Next Polymers Ltd. | PPS | Next PPS |
| AT 7205 | Celanese EVA Performance Polymers | LDPE | AT |
| Sylvin 6421-62 Natural | Sylvin Technologies Incorporated | TPE | Sylvin |