Niretan A 27 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DeabSv_Niretan-A-27-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyammide 66 mass coloured, easy flowing, for the injection moulding of items with low thickness, with short cycles and easy demoulding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 - 2.4 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 10 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | 95 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | |||
| Yield | 90.0 | 60.0 | MPa | ASTM D638 |
| Fracture | 85.0 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | -- | 80 | % | ASTM D638 |
| Flexural Modulus 3 | 3100 | 1300 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 130 | 60.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 40 | 70 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 60 | 120 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 260 | -- | °C | ASTM D3418 |
| CLTE - Flow | 9.0E-6 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 30 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 Tensile Elongation at Break, ASTM D638, 50 mm/min: ott |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-269H-1000 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| Sanren M3700C (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Thermoset Plastics 300 No.70 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| WPP PP WPP 204 | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Zythane® 8085D | Alliance Polymers & Services | TPU, Unspecified | Zythane® |