Geon™ Specialty Suspension Atlas S140
| Category: | PVC Homopolymer , Polyvinyl Chloride Homopolymer |
| Manufacturer: | Mexichem Specialty Resins, Inc. |
| Trademark: | Geon™ Specialty Suspension |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | De9rsY_Geon-Specialty-Suspension-Atlas-S140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon® Atlas S140 is high molecular weight homopolymer specialty suspension resin intended for use in high strength extruded parts. It improves the physical performance of end application for intsance wire and cable insulation, extruded tubes. The high porosity property of this resin allows rapid plasticizer absorption reducing the compound cycle times and resulting in high compound throughput and low manufacturing cost. Geon® Atlas S140 improves heat distortion (HDT) performance, increase the strength for highly plasticized formulas, and provides longer product shelf life. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| K-Value 1 | 82.0 | Internal method | |
| Contamination | Internal method | ||
| Dark Particles 2 | 1 | Internal method | |
| Light Colored Particles 3 | 4 | Internal method | |
| Magnetic Particles 4 | 0 | Internal method | |
| Apparent loose density 5 | 0.410 | g/cm³ | Internal method |
| Intrinsic Viscosity 6 | 1.4 | ASTM D1243-60-A | |
| Particle Size | Internal method | ||
| <105 micron 7 | 14.8 | % | Internal method |
| > 250 micron 8 | 3.40 | % | Internal method |
| Average Particle Size 9 | 145 | µm | Internal method |
| Relative Viscosity 10 | 3.10 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Optimal stretching 11 | 17.9 | MPa | ASTM D638 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Powder Mix Time 12 | 2.6 | min | Internal method |
| Residual Vinyl Chloride Monomer 13 | ppm | Internal method | |
| Volatiles 14 | 0.070 | % | Internal method |
| polymerization process | Suspension | ||
| Porosity 15 | 0.570 | cm³/g | Internal method |
| Flow time- Conditioned Funnel Flow Time 16 | 27.0 | sec | Internal method |
| Note:The value set forth represent 'typical' values and Mexichem Specialty Resins, therefore, makes no representation that the material in any particular shipment will conform to the listed properties.Packaging: This resin is shipped in multi-wall paper bags, netweight 50lbs, 2,500lbs per pallet. Information shown on the package includes commercial identification number, lot, and weight.STP 488 (formulation): 100phr Geon® Atlas S140, 55phr TOTM, and 18phr FillerASTM D638 (formulation): 100phr Geon® Atlas S140, 60phr DINP, 5phr ESO, and 2phr Mark 4716 |
| Note Message | |
|---|---|
| 1 . | Interrelationship |
| 2 . | Geon® 1217 |
| 3 . | Geon® 1005 |
| 4 . | Geon® STP 1217Unit: #/100in2 |
| 5 . | Geon® STP 1169 |
| 6 . | Puli 1386 |
| 7 . | Through the 140 net, Geon®812 |
| 8 . | Keep at 40 60 nets, Geon®812 |
| 9 . | Geon® DFT 1466 |
| 10 . | Interrelationship |
| 11 . | With provided formulation |
| 12 . | Geon® STP 488 with provided formulation |
| 13 . | Geon® STP 1005 |
| 14 . | Bags, Geon®793 |
| 15 . | Geon® 1094 |
| 16 . | Geon® STP 1169 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) LP 500 RCP | A. Schulman Europe | ABS | POLYMAN® |
| Razamid® B121 GR30 | Razin™ Engineering Plastics | Nylon 6 | Razamid® |
| HIVAL® 2420 NA | Nexeo Solutions, LLC. | PP Homopolymer | HIVAL® |
| Polifil® PP RMT-20V | The Plastics Group | PP, Unspecified | Polifil® PP |
| Pearlbond™ 550 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |