| PA 66, 30 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 300°C, 2.00mm 1 | 1.1 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 300°C, 2.00mm 3 | 0.40 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.040 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 230 | 130 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 10300 | 6790 | MPa | ASTM D638 |
| 23°C | 9500 | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 179 | 125 | MPa | ASTM D638 |
| Fracture, 23°C | 185 | 115 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 3.0 | 6.0 | % | ASTM D638 |
| Fracture, 23°C | 3.5 | 6.5 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 8400 | 5900 | MPa | ASTM D790 |
| 23°C 5 | 9200 | 5500 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 290 | 200 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 260 | 145 | MPa | ISO 178/A |
| 23°C 6 | 280 | 185 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.2 | 6.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 55 | 55 | kJ/m² | ISO 180/1U |
| 23°C | 65 | 70 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.90 | -- | J | ISO 6603-2 |
| 23°C | 2.50 | 4.20 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 800 | -- | N | ISO 6603-2 |
| 23°C | 1000 | 1100 | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 240 | -- | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 185 | -- | °C | ISO 75-2/C |
| Vicat Softening Temperature | > 230 | -- | °C | ISO 306/B50, ISO 306/B120 |
| Melting Temperature 9 | 262 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 40 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.50 | -- | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | -- | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.010 | -- | IEC 60250 | |
| 23°C, 1 MHz | 0.018 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 700 | -- | °C | IEC 60695-2-12 |
| 1.60 mm | 700 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6610/40 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| Abstron HI40B | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Cereplast Compostables® 6015 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| LNP™ LUBRICOMP™ LFL36E compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |
| SQUARE® SSR1502-40 | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |