Bakelite® UP 3620
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DdKrgH_Bakelite-UP-3620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Polyester moulding compound, mainly organically filled, styrene free, processing shrinkage as for phenolic moulding compounds, nonflammable, high surface quality, UL listed moulding compound 1,5 mm / V-0 (ALL) Application Areas Lamp housings, neon tubes end parts and bases, switch gears, watt hour meters housings and base plates |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.72 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.60 | % | |
| -- 2 | 0.75 | % | |
| Water Absorption - 24h/23C | 70.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 3 | 0.25 | % | |
| -- 4 | 0.25 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 250 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2/1 |
| Tensile Stress | 50.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| Flexural Stress 5 | 85.0 | MPa | ISO 178 |
| Compressive Stress | 180 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 75.0 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 6(1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 5.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.020 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, All) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 70.0 | °C | |
| Nozzle Temperature | 70.0 to 100 | °C | |
| Processing (Melt) Temp | 70.0 to 100 | °C | |
| Mold Temperature | 160 to 180 | °C | |
| Injection Pressure | > 10.0 | MPa | |
| Back Pressure | 0.500 to 1.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Compression |
| 2 . | Injection |
| 3 . | Injection |
| 4 . | Compression |
| 5 . | 2.0 mm/min |
| 6 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PP PRM3101 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Axiall PVC 7555 White | Axiall Corporation | PVC, Rigid | Axiall PVC |
| POLYCOMPO PE 401 | POLYCOMPO Co.,Ltd. | LDPE | POLYCOMPO PE |
| Eleme NGL150IG | Eleme Petrochemical Company Ltd | LLDPE | Eleme |
| Sylvin 4200-80UV Orange 5120 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |