Vyncolit® X7530
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dd7Roi_VyncolitX7530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X7530 is a glass fiber reinforced phenolic molding compound with superior mechanical properties : highest impact and excellent retention of mechanical properties at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Apparent Density | 0.58 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.14 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.010 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 1.5 | % | ISO 178 |
| Tensile Modulus | 17000 | MPa | ISO 527-2 |
| Tensile Stress | 123 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.95 | % | ISO 527-2 |
| Flexural Modulus | 16000 | MPa | ISO 178 |
| Flexural Stress | 245 | MPa | ISO 178 |
| Compressive Stress | 270 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 19 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 224 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.0E-5 | cm/cm/°C | TMA |
| Lateral | 4.1E-5 | cm/cm/°C | TMA |
| Thermal Conductivity | 0.37 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.9E+13 | ohms | IEC 60093 |
| Volume Resistivity | 7.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm, Tested by SBHPP) | V-1 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G20P252-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SEETEC EVA VS410 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| MOSTEN GA 506 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| Hanwha Total PP TB52M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| EMERGE™ PC 8701-15 | Trinseo | PC | EMERGE™ |