Taitalac® 6000F
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DcxiCg_Taitalac-6000F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitalac®6000F is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is extrusion. Taitalac®The main features of 6000F are:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 1.0 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C, 3.18mm | 34.5 | MPa | ASTM D638 |
| Fracture, 23°C, 3.18mm | 26.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.18 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | 2210 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 23°C) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.18 mm | 280 | J/m | ASTM D256 |
| 23°C, 12.7 mm | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 86.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Water Absorption, ASTM D570: <0.3% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 1088B | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Sinpolene MBB2507 | Teknor Apex Asia Pacific PTE. LTD. | Nylon, Unspecified | Sinpolene |
| Braskem PE TN7006 | Braskem | LDPE | Braskem PE |
| Hylon® N1200TL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina WHITE PVC COMP E 856-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |