LNP™ THERMOCOMP™ 9X10401H compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DceRUG_LNP-THERMOCOMP-9X10401H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X10401H is a compound based on Polyphenylsulfone containing proprietary filler(s). Added feature of this grade is: X-Ray Opaque. Also known as: LNP* THERMOCOMP* Compound 9X10401H Product reorder name: 9X10401H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.46 | g/cm³ | |
| -- | 1.45 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.80 to 1.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.26 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.47 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2660 | MPa | ASTM D638 |
| -- | 2550 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 72.0 | MPa | ASTM D638 |
| Yield | 71.0 | MPa | ISO 527-2/5 |
| Break 3 | 57.0 | MPa | ASTM D638 |
| Break | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/5 |
| Break 5 | 12 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2720 | MPa | ASTM D790 |
| -- 7 | 2580 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 86 | J/m | ASTM D256 |
| 23°C 8 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 9 | 180 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 34.0 | J | ASTM D3763 |
| -- | 29.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 213 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 203 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 200 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.3E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® FG01 | Guangdong Silver Age Sci & Tech. Co., Ltd | PVC, Rigid | SILVER® |
| Mylar® EL (400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Alathon® L5045 | LyondellBasell Industries | HDPE, MMW | Alathon® |
| Globalprene® 9557 | Lee Chang Yung Chemical Industry Corp. | SEBS | Globalprene® |
| Hanwha Total PP BJ350 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |