Generic PLA
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DbyeGP_Generic-PLA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PLA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 - 1.24 | g/cm³ | ASTM D792 |
| 23°C | 1.24 - 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 210°C/2.16 kg | 6.0 - 78 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 1.5 - 36 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.37 - 0.41 | % | ASTM D955 |
| 23°C | 0.30 - 1.1 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2020 - 3540 | MPa | ASTM D638 |
| 23°C | 310 - 5620 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 61.0 - 65.5 | MPa | ASTM D638 |
| Yield, 23°C | 15.5 - 72.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 48.8 - 56.2 | MPa | ASTM D638 |
| Fracture, 23°C | 13.8 - 70.0 | MPa | ISO 527-2 |
| 23°C | 47.8 - 68.9 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 9.8 - 10 | % | ASTM D638 |
| Yield, 23°C | 1.0 - 8.5 | % | ISO 527-2 |
| Fracture, 23°C | 0.50 - 9.2 | % | ASTM D638 |
| Fracture, 23°C | 1.0 - 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2390 - 4930 | MPa | ASTM D790 |
| 23°C | 305 - 9500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 47.9 - 110 | MPa | ASTM D790 |
| 23°C | 9.00 - 111 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.4 - 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 8.5 - 24 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 16 - 47 | J/m | ASTM D256 |
| 23°C | 3.4 - 6.4 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 49.7 - 52.3 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 50.0 - 120 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 - 50.2 | °C | ISO 75-2/A |
| Glass Transition Temperature | |||
| -- | 56.4 - 57.5 | °C | ASTM E1356 |
| -- | 43.8 - 62.5 | °C | DSC |
| Vicat Softening Temperature | 54.7 - 63.5 | °C | ISO 306 |
| Melting Temperature | 157 - 170 | °C | |
| Peak Crystallization Temperature (DSC) | 130 - 164 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 45.0 - 77.6 | °C | |
| Drying Time | 2.9 - 6.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.30 | % | |
| Rear Temperature | 150 - 185 | °C | |
| Middle Temperature | 170 - 210 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 190 - 205 | °C | |
| Processing (Melt) Temp | 178 - 240 | °C | |
| Mold Temperature | 16.0 - 107 | °C | |
| Injection Pressure | 78.4 - 79.3 | MPa | |
| Back Pressure | 0.500 - 1.10 | MPa | |
| Screw Speed | 75 - 153 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PLAThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 48.8 - 90.6 | °C | |
| Drying Time | 2.8 - 10 | hr | |
| Suggested Max Moisture | 5.0E-3 - 0.30 | % | |
| Cylinder Zone 1 Temp. | 164 - 190 | °C | |
| Cylinder Zone 2 Temp. | 166 - 192 | °C | |
| Cylinder Zone 3 Temp. | 168 - 206 | °C | |
| Adapter Temperature | 170 - 199 | °C | |
| Melt Temperature | 190 - 230 | °C | |
| Die Temperature | 165 - 200 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PLAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REDI-LINK™ DFDA-5430 NT | The Dow Chemical Company | LLDPE | REDI-LINK™ |
| Selvol™ 823 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Starpylen MFK42AS | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Chemlon® 109-13 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Karina IVORY PVC COMPOUND -E 818-35/ 1-Y-SN-ERM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |