TPX™ MBZ230(A)
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Dbkpz1_TPXMBZ230A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TPX™MBZ230(A) is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in North America and is processed by extrusion or injection molding. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 57 | g/10 min | Internal method |
| Spiral Flow 1 | 48.0 | cm | Internal method |
| Molding Shrinkage 2 | Internal method | ||
| Flow : 2.00mm | 1.5 | % | Internal method |
| Transverse flow : 2.00mm | 1.1 | % | Internal method |
| Water Absorption (Saturation) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 84 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 3(23°C, Injection Molded) | 2250 | MPa | ASTM D638 |
| Tensile Strength 4 | ASTM D638 | ||
| Yield, 23°C, injection molding | 27.0 | MPa | ASTM D638 |
| Fracture, 23°C, injection molding | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 5(Break, 23°C, Injection Molded) | 20 | % | ASTM D638 |
| Flexural Modulus 6(mm, injection molding, 51.0mm span) | 1820 | MPa | ASTM D790 |
| Flexural Strength 7(mm, injection molding, 51.0mm span) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 99 | J/m | ASTM D256 |
| Unnotched Izod Impact 8(23°C, Injection Molded) | 56 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 9(0.45 MPa, Unannealed, 6.35 mm) | 145 | °C | ASTM D648 |
| Vicat Softening Temperature | 162 | °C | ASTM D1525 10 |
| Peak Crystallization Temperature (DSC) | 233 | °C | ASTM D3418 |
| CLTE - Flow (-10 to 160°C) | 1.3E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 11(2.00 mm) | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 12(2.00 mm) | 28 | kV/mm | ASTM D149 |
| Dielectric Constant 13(2.00 mm, 1 MHz) | 2.38 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 20 - 60 | °C | |
| Injection Pressure | 30.0 - 40.0 | MPa | |
| Holding Pressure | 30.0 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 300°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 280 | °C | |
| Cylinder Zone 2 Temp. | 290 | °C | |
| Cylinder Zone 3 Temp. | 290 | °C | |
| Cylinder Zone 4 Temp. | 290 | °C | |
| Adapter Temperature | 290 | °C | |
| Die Temperature | 290 | °C |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 73°C, melt temperature: 310°C |
| 2 . | 260 to 280°C |
| 3 . | Type 4, 50mm/min |
| 4 . | Type 4, 50mm/min |
| 5 . | Type 4, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Partial Break |
| 9 . | 120°C/hr |
| 10 . | 速率 A (50°C/h), 压 力1 (10N) |
| 11 . | Injection Molded |
| 12 . | Injection Molded |
| 13 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SumiDurez 111 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| Xuchuan XCS-2086B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Nypol® PA B3 HL BRC0001 NT348 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| OmniLon™ PA6/6 S12 FD | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| TechnoFin PP EPDM T 10 | TechnoCompound GmbH | PP+EPDM | TechnoFin |