TARODUR 100 G3
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TARODUR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DacagY_TARODUR-100-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ABS glass fiber reinforced 17%, good dimensional stability, low shrinkage, good mechanical properties. Approved FIAT 55234 - 90.40 Available: all colors, UV stabilized (L), heat stabilized (H). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.10 to 0.30 | % | |
| Across Flow | 0.30 to 0.80 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.10 | % | ASTM D570, ISO 62 |
| Saturation | 0.20 | % | ASTM D570 |
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 78.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 1 | 75.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ASTM D1525, ISO 306/A50 3 2 |
| -- | 104 | °C | ASTM D1525, ISO 306/B50 4 3 |
| Ball Pressure Test (100°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 550 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 70.0 to 80.0 | °C | |
| Pre-heater | 70.0 to 80.0 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 20000 hrs |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sofprene T® 550100A60 | SO.F.TER. SPA | SBS | Sofprene T® |
| WELNEX™ RMG02 | Japan Polychem Corporation | PP Random Copolymer | WELNEX™ |
| LNP™ STAT-KON™ DE0026 compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| OLEFISTA™ QX0238B | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| Sumiliteresin® PR-54364 I | SBHPP | Phenolic | Sumiliteresin® |