Jampilen HP520H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Jam Polypropylene Company |
| Trademark: | Jampilen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Da6lif_Jampilen-HP520H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jampilen HP520H is a homopolymer designed for the production of biaxially oriented polypropylene films through a very stable extrusion on stenter and double bubble lines with excellent thickness control, increased drawability and readiness to a two way orientation. Jampilen HP520H contains a reinforced processing stabilization but does not contain any slip or antiblocking agents. BOPP films produced with this grade feature good mechanical properties, even at low temperatures, excellent barrier against moisture, odours, oils, fats and oxygen and high transparency, high gloss and good printability after corona treatment. Monolayer films made of Jampilen HP520H are used for food packaging, textiles packaging, flower wrappings and adhesive tapes. Jampilen HP520H is suitable for food contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 12 | % | ASTM D638 |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 1 |
| Accelerated Oven Ageing (150°C) | 500 | hr | ASTM D3012 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.30 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS H814 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| 3M™ Dyneon™ PTFE Compound TF 2274 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| DELPET™ 80NR | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| KOCETAL® VT702 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| KOPPS® S13G40BL | Kolon Plastics, Inc. | PPS | KOPPS® |