Amodel AS -1566 HS resin is a 65% glass fiber and mineral fiber reinforced polyphthalamide (PPA) resin with high deformation temperature and high bending modulus. This brand is specially developed for high cost-effective products requiring high rigidity, good dimensional stability and chemical resistance. Amodel AS -1566 HS resin Conventional applications include electrical connectors and housings, auto parts, pistons, covers, engine parts and transmission parts. -Black: AS-1566 HS BK 324 black: AS-1566 HS BK 545 natural color: AS-1566 HS NT

General Information
Filler / Reinforcement	Glass \mineral, 65% filler by weight
Additive	heat stabilizer
Features	Super rigidity Good dimensional stability Low CLTE High strength Good creep resistance Good chemical resistance Heat resistance, high Thermal Stability Good toughness
Uses	Lawn and Garden Equipment Power/other tools Valve/valve components Industrial components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Parts under the hood of a car Automotive Electronics Application in Automobile Field General Shell
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.84	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.30	--	%	ASTM D955
Transverse flow	0.50	--	%	ASTM D955
Water Absorption (24 hr)	0.10	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	20000	20900	MPa	ASTM D638
23°C	22500	--	MPa	ISO 527-2
100°C	17200	--	MPa	ISO 527-2
150°C	7310	--	MPa	ISO 527-2
175°C	6210	--	MPa	ISO 527-2
Tensile Strength
Fracture	207	--	MPa	ASTM D638
Fracture, 23°C	200	--	MPa	ISO 527-2
Fracture, 100°C	127	--	MPa	ISO 527-2
Fracture, 150°C	52.4	--	MPa	ISO 527-2
Fracture, 175°C	43.4	--	MPa	ISO 527-2
--	--	175	MPa	ASTM D638
Tensile Elongation
Fracture	1.7	1.8	%	ASTM D638
Fracture, 23°C	1.4	--	%	ISO 527-2
Fracture, 100°C	1.5	--	%	ISO 527-2
Fracture, 150°C	3.4	--	%	ISO 527-2
Fracture, 175°C	3.1	--	%	ISO 527-2
Flexural Modulus
--	18600	19900	MPa	ASTM D790
23°C	20500	--	MPa	ISO 178
100°C	16800	--	MPa	ISO 178
150°C	7310	--	MPa	ISO 178
175°C	6410	--	MPa	ISO 178
Flexural Strength
--	--	263	MPa	ASTM D790
23°C	284	--	MPa	ISO 178
100°C	205	--	MPa	ISO 178
150°C	95.8	--	MPa	ISO 178
175°C	75.8	--	MPa	ISO 178
Yield	290	--	MPa	ASTM D790
Shear Strength	80.0	62.7	MPa	ASTM D732

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.1	--	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	34	--	kJ/m²	ISO 179/1eU
Notched Izod Impact
--	64	53	J/m	ASTM D256
23°C	6.5	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact
--	590	--	J/m	ASTM D256
23°C	44	--	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	280	--	°C	ISO 75-2/A
1.8 MPa, annealed	278	--	°C	ASTM D648
Melting Temperature	311	--	°C	ISO 11357-3, ASTM D3418
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	1.7E-5	--	cm/cm/°C	ASTM E831
Flow : 100 to 200°C	1.7E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	4.0E-5	--	cm/cm/°C	ASTM E831
Lateral : 100 to 200°C	7.2E-5	--	cm/cm/°C	ASTM E831

Injection	Dry	Unit
Drying Temperature	120	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Hopper Temperature	79.4	°C
Rear Temperature	307 - 329	°C
Front Temperature	307 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	65.6 - 166	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	DZITUk_Amodel-AS-1566-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Polyvel PLA CN-L01 PLA Nucleating Agent	Polyvel Inc.	PLA	Polyvel PLA
Taitarex® 616	Taita Chemical Company, Ltd.	PS (HIPS)	Taitarex®
Network Polymers PC 1011	Network Polymers, Inc.	PC	Network Polymers PC
Bergadur™ PB40 natur TM-Z FD	PolyOne Corporation	PBT	Bergadur™
TOTAL Polystyrene Compound 881	TOTAL Refining & Chemicals	PS (HIPS)	TOTAL Polystyrene