Devcon Plastic Welder™
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Devcon |
| Trademark: | Devcon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DYNgrO_Devcon-Plastic-Welder-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toughened structural adhesive, after curing, produces superior strength to load-bearing bonds to engineered plastics. Intended Use:
Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Volume | 1.02 | cm³/g | |
| Solid content- by Volume | 100 | % |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Impact Resistance | 46.2 | kJ/m² |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -55 - 121 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time (22°C) | 4.0 - 6.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Shear Adhesion | ASTM D1002 | ||
| ABS | 8.96 | MPa | ASTM D1002 |
| GBS | 24.1 | MPa | ASTM D1002 |
| Polycarb | 9.65 | MPa | ASTM D1002 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.983 | g/cm³ |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Elongation (Break) | 15 - 25 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Component B | Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0 | ||
| Thermoset Mix Viscosity | 50000 | cP |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cured 7 days @ 75°F |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Curing Time | 24 | hr |
| Note Message | |
|---|---|
| 1 . | Mixed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| KOPA® KN333HRN | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Karina BLACK PVC COMPOUND 603-48/1-Y-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| Optix® CP-86 UVA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| OTECH ALLOY OW127 - Cord Jacket | OTECH Corporation | TP, Unspecified | OTECH ALLOY |