TRANSMARE® 22CT25-0.001
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DYMGZe_TRANSMARE-22CT25-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 22CT25-0.001 is a 25% talc filled polypropylene copolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 2750 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 27.0 | MPa | |
| Break, 4.00 mm | 23.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 2.7 | % | |
| Break, 4.00 mm | 13 | % | |
| Flexural Modulus | 2700 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 1.2 | kJ/m² | |
| 23°C | 2.7 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 23 | kJ/m² | |
| 23°C | 49 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.1 | kJ/m² | |
| 23°C | 3.8 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 18 | kJ/m² | |
| 23°C | 41 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 6323F | Formosa Plastics Corporation | LDPE | TAISOX |
| DAI-EL™ G-7251 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| FHR Polypropylene 23S1Acs256 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| EPO-TEK® 353ND-T1 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina GRAY PVC COMPOUND 800-18/233-A-ERYB (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |