KumhoSunny PPO HPP8340
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DYMEbe_KumhoSunny-PPO-HPP8340.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HPP8340 is general purpose PS/PPE resin. HPP8340 has high heat resistance. HPP8340 is mainly used in automobile inner & outer decorations, fluid engineering,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 to 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 1510 | MPa | ASTM D790 |
| Flexural Strength | 45.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 150 | °C | ASTM D648 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 2.00 to 6.00 | MPa | |
| Screw Speed | 40 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Polyethylene B128 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| ACRYLITE® Sheet GMS | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® Sheet |
| APEX® 3210-55NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ESPRENE EPDM 606F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| Osterlene® HE-3-2 | Osterman & Company | PS (HIPS) | Osterlene® |