Order Products : sales@su-jiao.com
TECNOBLEND B35 G2
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TECNOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DXEzc4_TECNOBLEND-B35-G2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/PA alloy 8% glass fibres reinforced combining excellent dimensional stability, very good impact strength, stiffness and chemical resistance with good surface appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 23°C, 3.20mm | 0.80 | % | Internal method |
| Flow direction : 23°C, 3.20mm | 0.50 | % | Internal method |
| Water Absorption (Saturation, 23°C) | 1.4 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(750°C) | 8.0 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 54.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 2850 | MPa | ISO 178 |
| Flexural Stress 4 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.5 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -20°C | 60 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| -30°C | 5.8 | kJ/m² | ISO 180/1A |
| Notched Izod Impact (23°C) | 12.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, not annealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ISO 306/A50 |
| -- | 115 | °C | ISO 306/B50 |
| CLTE - Flow (-30 to 30°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 6(1.60 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | US FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Glas® 3100-15 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| Evermore PUR SA-700 | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Ferro PP TPP20AN64NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| omay® SC42 | Suzhou OMAY Optical Materials Co., Ltd | Film, PP | omay® |
| OmniLon™ PA612 GR40 | OMNI Plastics, LLC | Nylon 612 | OmniLon™ |