Reny® 1038
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DWzWO2_Reny-1038.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1038 is a Polyarylamide (PARA) material filled with 60% long glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1038: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.76 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.41 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 26700 | 21300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 262 | 259 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.3 | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 24000 | 23000 | MPa | ISO 178 |
| Flexural Stress | 477 | 409 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | 36 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | 86 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 239 | 236 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 234 | 227 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E General Purpose G-4680E | S&E Specialty Polymers, LLC | PVC, Flexible | S&E General Purpose |
| Sylvin 8215-65FUV White 1561 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dryflex® SE 75A201 | ELASTO | TPE | Dryflex® |
| Sylvin 4240-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PE SGD4960 | Braskem America Inc. | HDPE | Braskem PE |