Romiloy® 6020 F
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DViurd_Romiloy-6020-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®6020 F is an acrylonitrile-styrene-acrylate PC (ASA PC) material,. This product is available in Europe and is processed by extrusion or injection molding. Romiloy®The main features of 6020 F are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 50 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 - 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 70 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 126 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 55°C) | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901.The value listed as Coefficient of Linear Thermal Expansion ISO 11359-1-2, was tested in accordance with DIN 53752. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 5 | % | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Back Pressure: <20%Holding Pressure: Low |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Cylinder Zone 1 Temp. | 210 - 250 | °C | |
| Cylinder Zone 2 Temp. | 210 - 250 | °C | |
| Cylinder Zone 3 Temp. | 210 - 250 | °C | |
| Cylinder Zone 4 Temp. | 210 - 250 | °C | |
| Cylinder Zone 5 Temp. | 210 - 250 | °C | |
| Melt Temperature | < 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T GREY 5161 MAC | Arkema | Nylon 11 | Rilsan® Fine Powders |
| RTP 300 GB 20 TFE 15 FR | RTP Company | PC | RTP |
| Next Nylon 6 Industrial Series NG30-02JBK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| Hax™ HF 28 | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| Hylon® N1035STL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |