PELPRENE™ S1001
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PELPRENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DVSVuR_PELPRENE-S1001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PELPRENE™S1001 is a thermoplastic polyester elastomer (TPEE) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.2 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 65% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 48 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 730 | % | ASTM D638 |
| Flexural Modulus | 125 | MPa | ASTM D790 |
| Compressive Modulus | 10.2 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles) | 15.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (50% Strain) | 10.8 | MPa | ASTM D412 |
| Tear Strength | 118 | kN/m | ASTM D624 |
| Compression Set | 60 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.0 | °C | ASTM D648 |
| Brittleness Temperature | -65.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 172 | °C | ASTM D1525 |
| Melting Temperature | 200 | °C | DSC |
| CLTE - Flow | 1.9E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Hardness, JIS k6301, A scale: 9610% Compression Modulus, ASTM D695: 10.2 MPaResilience, JIS K6301: 63 %Brittle Point, JIS K6301: < -65 °CCompression Set, JIS K6301: 60 %Coefficient of Linear Thermal Expansion, TMA: 19e-5 1/K |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 52GB001 | Reliance Industries Limited | HDPE, HMW | RELENE® |
| Borealis PP RJ470MO | Borealis AG | PP Random Copolymer | Borealis PP |
| EPLAMID 6 GFR 33 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| LONGLITE® PMC T391 | CCP Group | Phenolic | LONGLITE® PMC |
| Dryflex® SE 75A001 | ELASTO | TPE | Dryflex® |