EMLON® 6 GBR 20 FR V0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EMAS Plastik San.Tic.AS. |
| Trademark: | EMLON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DVD2B7_EMLON-6-GBR-20-FR-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, %20 glass beads reinforced, V0 flammability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 to 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.25 to 0.45 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 to 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 to 5000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 to 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 9.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | > 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | VDE 0471/2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2430F | Teknor Apex Company | TPE | Telcar® |
| TYNE® Olefins W6224 | Tyne Plastics LLC. | PP Copolymer | TYNE® Olefins |
| Cevian®-V LMW011 | PlastxWorld Inc. | ABS | Cevian®-V |
| Lion Idemitsu Composites PPS Y551F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| DEXFLEX® E756-1 BLK | LyondellBasell Industries | TPO (POE) | DEXFLEX® |