Ravago Compounds PP-5343
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Ravago Compounds |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DV30gg_Ravago-Compounds-PP-5343.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Key Features:
Colors:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 - 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 - 18 | g/10 min | ASTM D1238 |
| Carbon Black Content 1 | 0.80 - 1.2 | % | ASTM D1603 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | > 21.0 | MPa | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | > 1930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | > 40 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | > 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | > 73.3 | °C | ASTM D648 |
| Thermal stability- 1000 hours (150°C) | Pass | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 93.3 | °C | |
| Drying Time | 0.0 - 8.0 | hr | |
| Rear Temperature | 193 - 238 | °C | |
| Middle Temperature | 193 - 238 | °C | |
| Front Temperature | 193 - 238 | °C | |
| Nozzle Temperature | 193 - 238 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Back Pressure | 0.00 - 0.689 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Injection instructions |
|---|
| Hot Runner Temperature (if applicable): 420 to 450°F |
| Note Message | |
|---|---|
| 1 . | PP-5343-9000 only |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8300 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Mowital® B 45 M | Kuraray Co., Ltd. | PVB | Mowital® |
| NEFTEKHIM PP 8340N (EPF31HR) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Baoding 6150 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Hyundai EP PA6 LS135 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |