RTP 1382 AR 15
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DUvX6U_RTP-1382-AR-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Preliminary Product Data per RTP Co. Carbon and Aramid Fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.050 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 26200 | MPa | ASTM D638 |
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 19300 | MPa | ASTM D790 |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Coefficient of Friction (With Metal-Dynamic) | 0.12 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 1mil/in.Tensile Elongation, ASTM D-638: 0-1%Wear Factor, K, ASTM D-3702: 160E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.12The wear factor and coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 302 - 343 | °C | |
| Middle Temperature | 302 - 343 | °C | |
| Front Temperature | 302 - 343 | °C | |
| Mold Temperature | 65.6 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1281-60D | RTP Company | TPU-Polyester | RTP |
| Primefin V500TL20 | Lucent Polymers, Inc. | PP Homopolymer | Primefin |
| CP PRYME® Acetal AC125G | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| OpteSTAT™ PA4,6 DP505x3 | Ovation Polymers Inc. | Nylon 46 | OpteSTAT™ |
| Geon™ Vinyl Flexible B5546 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |