Fortron® 0309
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DUXim1_Fortron-0309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 0309 exhibits a good balance of flow and melt strength for extrusion processes. The material demonstrates excellent heat and chemical resistance. The intended use of this product is for extruding monofilament/fibers. Available standard in powder (0309B4), pellet (0309P4) and crystallized pellet (0309C4) form. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 | g/cm³ | ASTM D792 |
| -- | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 - 1.2 | % | ASTM D955 |
| Transverse flow | 0.80 - 1.0 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 93 | ASTM D785 | |
| M scale | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 4200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 145 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 95.0 | °C | ISO 75-2/C |
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 5.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 1.0E+7 | ohms·cm | ASTM D257 |
| -- | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 3 | 18 | kV/mm | ASTM D149 |
| -- | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.00 | ASTM D150 | |
| 1 MHz | 3.00 | ASTM D150 | |
| 1 MHz | 4.60 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 1.1E-3 | IEC 60250 | |
| Arc Resistance | 124 | sec | ASTM D495 |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 1830 | J/kg/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 300 - 310 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Nozzle Temperature | 300 - 310 | °C | |
| Processing (Melt) Temp | 310 - 320 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 40.0 - 80.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 60.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 310 to 320°CZone 4 Temperature: 310 to 320°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW0551 | Teknor Apex Asia Pacific PTE. LTD. | LLDPE | Sinpolene |
| Borlink™ LE0310-04 | Borealis AG | PE, Unspecified | Borlink™ |
| Formolon® 622S | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |
| Petrothene® NA940 | LyondellBasell Industries | LDPE | Petrothene® |
| ESTOPLAST XU 6515NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |