Order Products : sales@su-jiao.com
DOWLEX™ 2106GC
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DTV4H2_DOWLEX-2106GC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2106GC is processable at high line speeds. Films made from DOWLEX 2106GC Polyethylene Resin exhibit excellent stretchability, tear and impact resistance, as well as exceptional optical properties. Applications:
Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 23 µm, extruded film | 6.20 | MPa | ASTM D882 |
| TD : Yield, 23 µm, extruded film | 5.50 | MPa | ASTM D882 |
| MD : Fracture, 23 µm, extruded film | 38.0 | MPa | ASTM D882 |
| TD : Fracture, 23 µm, extruded film | 21.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Fracture, 23 µm, extruded film | 500 | % | ASTM D882 |
| TD : Fracture, 23 µm, extruded film | 780 | % | ASTM D882 |
| Dart Drop Impact 3(23 µm, Cast Film) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength 4 | ASTM D1922 | ||
| MD : 23 µm, cast film | 320 | g | ASTM D1922 |
| TD : 23 µm, cast film | 530 | g | ASTM D1922 |
| Film tensile properties-maximum stretch to penetration- Cast Film 5(23.0 µm) | 160 | % | Internal method |
| Film tensile properties-maximum elongation- Cast Film 6(23.0 µm) | 260 | % | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 7(45°, 23.0 µm, Cast Film) | 93 | ASTM D2457 | |
| Haze 8(23.0 µm, Cast Film) | 0.60 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 280 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions For Cast Film: Melt Temperature: 220 - 280°C Chill Roll Temperature: 20 - 60°C Haul-Off Speed: 150 - 450 m/min Recommended Gauge Range: 10 - 60 µm |
| Note Message | |
|---|---|
| 1 . | 250 m/min; Chill roll 25°C |
| 2 . | 250 m/min; Chill roll 25°C |
| 3 . | 250 m/min; Chill roll 25°C |
| 4 . | Method B; 250 m/min; Chill roll 25°C |
| 5 . | 250 m/min; Chill roll 25°C; Measured on test stand; Max pre-stretch before sharp probe penetrates |
| 6 . | 250 m/min; Chill roll 25°C; Measured on test stand |
| 7 . | 250 m/min; Chill roll 25°C |
| 8 . | 250 m/min; Chill roll 25°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3567EU-01 CLEAR | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Fainplast PVC GS 75/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| JSR EPR EP01P | JSR Corporation | EPDM | JSR EPR |
| LNP™ STAT-KON™ OE004A compound | SABIC Innovative Plastics Europe | PPS, Branched | LNP™ STAT-KON™ |
| Sylvin 916VO-85 White 1481 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |