Shinko-Lac® ABS GL-4
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DTNGGR_Shinko-Lac-ABS-GL-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS GL-4 is a standard grade of ABS that features an ultra-high modulus along with an excellent balance of rigidity, strength, processability and glossiness. Typical applications of GL-4 include musical instruments, cosmetic containers, cassette recorders and stationery goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.9 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2940 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 58.8 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 3040 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 98.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 20 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 39 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 95.0 | °C | ASTM D648 |
| CLTE - Flow | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF5CGN (Series: FC) | KRAIBURG TPE | TPE | THERMOLAST® K |
| XANTAR® 25 U | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Iupilon® MB5002R | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |
| LGH 301 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |
| LNP™ THERMOCOMP™ RZ006SXP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |