Quadrant EPP Nylatron® 703 XL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DT4v6a_Quadrant-EPP-Nylatron-703-XL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nylatron® 703 XL sets a new standard of machined part performance for linear bearing and wear pad applications. Building on the success of Quadrant Engineering Plastic Products Nylatron® NSM, the industry's premier material for nearly 20 years, Nylatron 703 XL provides lifting equipment with a new advantage. The wear resistance of NSM with added benefit of zero "slip-stick" makes Nylatron 703 XL an ideal material for applications where precise motion control is required. Units equipped with Nylatron 703 XL can accurately display smaller movements made possible by today's sophisticated control devices. Static and dynamic coefficients of friction that approximate each other at virtually every point over the product's useful range, make this possible. Quadrant developed Nylatron 703 XL to meet the increasing needs of engineers in the construction and production equipment industries. Materials like Nylatron® NSM and Nylatron® GSM are still available, and are widely used in critical bearing applications. Quadrant offers a broad range of bearing and wear resistant materials that can handle aggressive thermal, wear and chemical environments. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.47 | % | |
| Saturation | 7.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | % | ASTM D638 |
| Flexural Modulus | 2480 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Compressive Modulus | 2480 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 68.9 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.14 | Internal Method | |
| Wear Factor | 52 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 93 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.596 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 216 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+12 | ohms | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rigid Cast RC-8004 FR | BJB Enterprises, Inc. | PUR, Unspecified | Rigid Cast |
| Advanced Composites BJS-MNR2 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| Innothane® IE-3050 | Innovative Polymers, Inc. | TSU | Innothane® |
| LUVOCOM® 1105-0699-F | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Durethan® AKV 35 XTS1 901510 | LANXESS GmbH | Nylon 66 | Durethan® |