Petrothene® NA967000
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DT4FSD_Petrothene-NA967000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA967000 is a low density polyethylene resin designed for blown film, general purpose and industrial packaging applications. NA967000 exhibits good processing characteristics and impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 10.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 179 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 228 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm, Blown Film | 24.8 | MPa | |
| TD : Yield, 32 µm, Blown Film | 17.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 220 | % | |
| TD : Break, 32 µm, Blown Film | 520 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, Blown Film | 390 | g | |
| TD : 32 µm, Blown Film | 100 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched LTB | 1 | °C | ASTM D746 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 Z | RTP Company | Nylon 66 | RTP |
| Tarnoform® 500 GF8 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Borlink™ LE0520 | Borealis AG | PE, Unspecified | Borlink™ |
| Dryflex® A1 600501 | ELASTO | SEBS | Dryflex® |
| Karina BLACK PVC COMPOUND 750-48/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |