INNOPOL® CS 1-5820 SA is a 20 % glass-fibre filled polypropylene homopolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 1-5820 SA is recommended for producing injection moulded products, where the required properties are high strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/2 |
| Tensile Stress (Yield) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 4400 | MPa | ISO 178 |
| Flexural Stress 2 | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 138 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A |
| -- | 125 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | FMVSS 302 | |
| flammability- Automotive materials (thickness d > 1 mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 240 | °C | |
| Middle Temperature | 190 - 240 | °C | |
| Front Temperature | 190 - 240 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 - 100 % of injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7693 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Resiten® 128 | ITEN INDUSTRIES | Phenolic | Resiten® |
| RheTech Polypropylene GC30P200-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| ADMER™ QF460E | Mitsui Chemicals Europe GmbH | PP, Unspecified | ADMER™ |
| Ferro PP TPP40AJ20NA | Ferro Corporation | PP Homopolymer | Ferro PP |