Amilan® CM3007 is a Polyamide 66 (Nylon 66) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
| 1.00 mm 1 | 0.80 to 1.5 | -- | % | |
| 3.00 mm 2 | 1.5 to 2.2 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.2 | -- | % | |
| Saturation, 23°C | 8.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| R-Scale, 80°C | 97 | -- | ||
| R-Scale, 23°C | 119 | 100 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 115 | 110 | MPa | |
| 23°C | 80.0 | 50.0 | MPa | |
| 80°C | 40.0 | 40.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 1.5 | -- | % | |
| Break, 23°C | 25 | 50 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 4300 | 4100 | MPa | |
| 23°C | 2900 | 1400 | MPa | |
| 80°C | 900 | 500 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 140 | 125 | MPa | |
| 23°C | 115 | 65.0 | MPa | |
| 80°C | 65.0 | 40.0 | MPa | |
| Compressive Stress (23°C) | 90.0 | -- | MPa | ISO 604 |
| Shear Strength (23°C) | 75.0 | 70.0 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 8.00 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 to 0.200 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 2.5 | -- | kJ/m² | |
| 23°C | 4.0 | 24 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | No Break | -- | ||
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 220 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 9.0E-5 to 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 2100 | -- | J/kg/°C | |
| Thermal Conductivity | 0.32 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 to 1.0E+15 | 1.0E+12 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 18 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 4 | IEC 60250 | |||
| 23°C, 50 Hz | 4.00 | 7.50 | ||
| 23°C, 1 kHz | 3.90 | 6.50 | ||
| 23°C, 1 MHz | 3.30 | 3.80 | ||
| Dissipation Factor 5 | IEC 60250 | |||
| 23°C, 50 Hz | 0.030 | 0.060 | ||
| 23°C, 1 kHz | 0.030 | 0.060 | ||
| 23°C, 1 MHz | 0.020 | 0.070 | ||
| Arc Resistance 6 | 130 | -- | sec | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.397 mm) | V-2 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1mm |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3489 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sindustris PP HF5158 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| SUSTAPEI MG | Röchling Sustaplast SE & Co. KG | PEI | SUSTAPEI |
| Tisoplen® PPC 30 MNF TALC | Tisan | PP Copolymer | Tisoplen® |
| Wellamid® GF13-66 22LH-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |