Order Products : sales@su-jiao.com
LNP™ VERTON™ NV0081EV_GY7E149 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DRkXHt_LNP-VERTON-NV0081EV-GY7E149-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Preliminary data for 40% long fiber single pellet non-halogen FR color filled PC/ABS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.060 to 0.26 | % | |
| Across Flow : 24 hr | 0.31 to 0.51 | % | |
| Water Absorption | |||
| 24 hr | 0.057 | % | ASTM D570 |
| 23°C, 24 hr | 0.075 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12300 | MPa | ASTM D638 |
| -- | 10800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 92.0 | MPa | ASTM D638 |
| Yield | 100 | MPa | ISO 527-2/5 |
| Break 3 | 92.0 | MPa | ASTM D638 |
| Break | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.90 | % | ASTM D638 |
| Yield | 0.90 | % | ISO 527-2/5 |
| Break 5 | 0.90 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 12900 | MPa | ASTM D790 |
| -- 7 | 12400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 152 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 156 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 156 | MPa | ASTM D790 |
| Flexural Strain at Break 10 | 1.3 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 300 | J/m | ASTM D256 |
| 23°C | 250 | J/m | ASTM D256 |
| -40°C 11 | 29 | kJ/m² | ISO 180/1A |
| 23°C 12 | 26 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -40°C | 480 | J/m | ASTM D4812 |
| 23°C | 440 | J/m | ASTM D4812 |
| -40°C 13 | 27 | kJ/m² | ISO 180/1U |
| 23°C 14 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 11.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 15 | 89.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.55 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 30.0 to 40.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 205 to 235 | °C | |
| Middle Temperature | 210 to 245 | °C | |
| Front Temperature | 215 to 245 | °C | |
| Processing (Melt) Temp | 220 to 255 | °C | |
| Mold Temperature | 35.0 to 65.0 | °C | |
| Back Pressure | 0.150 to 0.300 | MPa | |
| Screw Speed | 12 to 40 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 2 mm/min |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vistalon™ 3702 | ExxonMobil Chemical | EPDM | Vistalon™ |
| Dynaflex™ G7980-9 NSFG | PolyOne Corporation | TPE | Dynaflex™ |
| Epolene® C-17P | Westlake Chemical Corporation | LDPE | Epolene® |
| KOPELEN JI-360 | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Lushan EF-3 | Guangzhou Lushan New Materials Co., Ltd | Polyolefin, Unspecified | Lushan |