NYCOA Polyamide 2012
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DRi2gq_NYCOA-Polyamide-2012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2012 is a flexible Nylon copolymer TPE particularly suitable for extrusion and injection molding applications. It has a moderately high melt viscosity, excellent processability and yields extremely tough and resilient finished articles. NYCOA 2012 is recommended for applications that demand easy flow, exceptional toughness, and flexibility with low moisture absorption. Its melt viscosity and strength provide ease of processing for tubing, profile, and molded articles. The high thermal an NYCOA 2012 possesses excellent impact resistance and flexibility, without the use of plasticizer or other exuding additives. It is available with custom additive packages: heat stabilizer, UV stabilizer, flame retardant and/or customer colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.0 | % | ASTM D570 |
| Saturation | 5.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 300 | % | ASTM D638 |
| Flexural Modulus 3 | 1380 | MPa | ASTM D790 |
| Flexural Strength 4 | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 205 | °C |
| Additional Information |
|---|
| Water Extractable, NYCOA Method: 0.8 %The value listed as Melting Point was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638: 300+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terraloy™ BP-18003A | Teknor Apex Company | TPS+HIPS | Terraloy™ |
| Cevian®-V SKG10 | Daicel Polymer Ltd. | ABS | Cevian®-V |
| DOMAMID® 6AVUV | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| KYOCERA KE-G3000DA | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| Dow Corning® C6-180 | Dow Corning Corporation | Silicone | Dow Corning® |