Infino NH-1015V
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DRgizp_Infino-NH-1015V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino NH-1015V is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 64.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Break | 48.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 45 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 2 | 2400 | MPa | ASTM D790 |
| -- 3 | 2550 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 87.0 | MPa | ASTM D790 |
| -- 5 | 89.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C 7 | 14 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 94.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 86.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 82.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 97.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/B50 |
| -- | 103 | °C | ISO 306/B120 |
| RTI Elec (1.50 mm) | 90.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 85.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 90.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | Thickness: 4 mm |
| 7 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® eXten D 247F NATURAL | Solvay Engineering Plastics | Nylon 66/610 | TECHNYL® eXten |
| SLOVALEN® PC 51 C 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| ALTECH® PP-H A 2020/550 GF20 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Cri-Line SP-612 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Osterlene® CI-14-00 | Osterman & Company | PS (GPPS) | Osterlene® |