OmniPro™ HPP CCF20
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DRRGvB_OmniPro-HPP-CCF20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% CaCO 3 Reinforced, Homopolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 113 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 82.2 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 141 HI HF | RTP Company | PP Copolymer | RTP |
| WELLAMID Nylon 6600 CF 10 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Europrene® BR HV80 | Versalis S.p.A. | Rubber | Europrene® |
| Karina BLACK PVC COMPOUND 753-48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LSG1001-09A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |