Zytel® HTN 54G15HSLR BK031
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DRFqQk_Zytel-HTN-54G15HSLR-BK031.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Glass Reinforced, Toughened, PPA, High Performance Polyamide |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.40 | -- | % | |
| Viscosity Number (96% H2SO4 (Sulphuric Acid)) | 82.0 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 6100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 125 | 118 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 4900 | -- | MPa | ISO 178 |
| Flexural Stress | 210 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 5.0 | -- | kJ/m² | |
| 23°C | 6.0 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 60 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 277 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 300 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.4E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 3.4E-5 | -- | cm/cm/°C | |
| Transverse | 7.3E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 7.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.800 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SI-LINK™ DFDA-6451 NT | The Dow Chemical Company | PE Copolymer | SI-LINK™ |
| Daelim Po1y® LH6070S | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DENKA ABS K-5120G | Denka Company Limited | ABS | DENKA ABS |
| Elastron® D D101.A72.N | Elastron USA, Inc. | SBS | Elastron® D |
| Rotuba CAB B9004 (7% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |