BioFibra® BF-LED01
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | FuturaMat |
| Trademark: | BioFibra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DQVf6c_BioFibra-BF-LED01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BF-LED01 is an agromaterial descending from the BioFibra range. BF-LED01 is a wood fibers (spruce)-based product an is 100% from renewable ressources. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 to 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 5.6 to 17 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 71 to 85 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 to 3740 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 to 41.0 | MPa | |
| Break | 22.0 to 36.0 | MPa | |
| Tensile Strain (Yield) | 1.3 to 2.1 | % | ISO 527-2 |
| Flexural Modulus | 3200 to 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 7.0 to 13 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 38.0 to 46.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-1195B BLK X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| SHIN-A SEV-4335M70 | SHIN-A T&C | Epoxy | SHIN-A |
| ACCUTECH™ HP0334C30L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| EXCELLOY CK10G20 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| Karina BLACK PVC COMPOUND 751-48/ 1-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |