Latamid 66 H2PX-V2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DPuhqG_Latamid-66-H2PX-V2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on Polyamide 66 (PA 66). Heat stabilised. Toughened. UL94 V-2 classified, with halogens, PBB/PBDE free. Product UL certified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.5 | % | |
| Flow : 2.00 mm | 1.2 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2500 | MPa | |
| 60°C | 1250 | MPa | |
| 90°C | 700 | MPa | |
| 120°C | 500 | MPa | |
| 150°C | 350 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 60.0 | MPa | |
| Break, 23°C | 55.0 | MPa | |
| Break, 60°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 15 | % | |
| Break, 60°C | 80 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 55 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 95.0 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BI12NT6521 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| VAMPSTAT A 00U 04 V0 26 | Vamp Tech | ABS | VAMPSTAT |
| CP PRYME® Polypropylene PPC100NB-20M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |
| Flontech® FT-GL15-M5-3 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Karina NATURAL PVC COMPOUND -E 890-25/ 1-CR-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |