Eltex® PF6130LA
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | Eltex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DPeuSG_Eltex-PF6130LA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Eltex ® PF6130LA is particularly suitable for high performance cast stretch film applications, in both monolayer and co-extruded structures. It is designed for applications which require a very low level of gels. It also can be used for the production of artificial grass monofilaments. Benefits and Features Eltex ® PF6130LA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. Eltex® PF6130LA offers the following properties:
We recommend that you consult your INEOS technical representative for further advice on the use of Eltex® PF6130LA. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% Secant, MD : 20 µm | 115 | MPa | |
| 1% Secant, TD : 20 µm | 120 | MPa | |
| Tensile Stress | ISO 1184 | ||
| MD : Break, 20 µm | 40.0 | MPa | |
| TD : Break, 20 µm | 20.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 20 µm | 300 | % | |
| TD : Break, 20 µm | 400 | % | |
| Dart Drop Impact (20 µm) | 600 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 260 | g | |
| TD : 25 µm | 430 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 93 | ASTM D2457 | |
| Haze (20.0 µm) | 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance | 28.0 | Ncm/µ | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | Conditioning ISO 1872/1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake LDPE EF602 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Five Plus™ CPP40C | Noble Polymers | PP Copolymer | Five Plus™ |
| Elvax® 3128-1 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Hanwha Total PP FE17 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| ICORENE® 1506 BLACK 9001 | A. Schulman Europe | XLPE | ICORENE® |