Generic Nylon 6 - Glass Fiber
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DPN69C_Generic-Nylon-6---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 - 1.57 | g/cm³ | ASTM D792 |
| 23°C | 1.19 - 1.56 | g/cm³ | ISO 1183 |
| -- | 1380 | kg/m³ | ISO 1183 1 |
| -- | 1.22 - 1.44 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 235°C/2.16 kg | 2.7 - 25 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 1.7 - 3.1 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 24.1 - 60.3 | cm³/10min | ISO 1133 |
| Spiral Flow | 34.5 - 95.0 | cm | |
| Molding Shrinkage | |||
| Flow : 23°C | 0.10 - 0.78 | % | ASTM D955 |
| Transverse flow : 23°C | 0.48 - 1.2 | % | ASTM D955 |
| 23°C | 0.051 - 1.1 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.55 - 1.4 | % | ASTM D570 |
| 23°C, 24 hr | 0.62 - 1.7 | % | ISO 62 |
| Saturated, 23°C | 0.10 - 7.6 | % | ASTM D570 |
| Saturated, 23°C | 4.3 - 8.2 | % | ISO 62 |
| Saturation | 6.6 | % | ISO 62 2 |
| Equilibrium, 23°C | 0.24 - 2.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 - 2.5 | % | ISO 62 |
| Balance | 1.7 | % | ISO 62 3 |
| Viscosity Number | |||
| -- | 145 - 153 | cm³/g | ISO 307 |
| -- | 145 | cm³/g | ISO 307, 1157, 1628 4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 115 - 123 | ASTM D785 | |
| 23°C | 114 - 123 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 80 - 85 | ASTM D2240 | |
| 23°C | 77 - 89 | ISO 868 | |
| Ball Indentation Hardness | 168 - 283 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 4630 - 13500 | MPa | ASTM D638 |
| 23°C | 4600 - 16600 | MPa | ISO 527-2 |
| -- | 8680 | MPa | ISO 527-2 5 |
| Tensile Strength | |||
| Yield, 23°C | 83.0 - 222 | MPa | ASTM D638 |
| Yield, 23°C | 68.2 - 210 | MPa | ISO 527-2 |
| Fracture, 23°C | 79.3 - 222 | MPa | ASTM D638 |
| Fracture, 23°C | 80.0 - 236 | MPa | ISO 527-2 |
| Fracture | 141 | MPa | ISO 527-2 6 |
| 23°C | 82.1 - 210 | MPa | ASTM D638 |
| 23°C | 105 - 223 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.4 - 5.1 | % | ASTM D638 |
| Yield, 23°C | 1.9 - 4.2 | % | ISO 527-2 |
| Fracture, 23°C | 1.0 - 5.5 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 4.9 | % | ISO 527-2 |
| Fracture | 3.0 - 3.1 | % | ISO 527-2 7 |
| Flexural Modulus | |||
| 23°C | 3200 - 11200 | MPa | ASTM D790 |
| 23°C | 3600 - 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 114 - 305 | MPa | ASTM D790 |
| 23°C | 136 - 327 | MPa | ISO 178 |
| Yield, 23°C | 148 - 320 | MPa | ASTM D790 |
| Fracture, 23°C | 99.4 - 285 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 27.4 - 241 | MPa | ASTM D695 |
| Shear Strength (23°C) | 66.7 - 100 | MPa | ASTM D732 |
| Coefficient of Friction | 0.15 - 0.36 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 10.0 - 30.5 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23°C | 44.1 - 119 | J/m | ASTM D256 |
| 23°C | 3.0 - 21 | kJ/m² | ISO 179 |
| -30°C | 9.00 | kJ/m² | ISO 179/1eA 8 |
| 23°C | 10.6 | kJ/m² | ISO 179/1eA 9 |
| Charpy Unnotched Impact Strength | |||
| 23°C | 29 - 100 | kJ/m² | ISO 179 |
| -30°C | 47.5 | kJ/m² | ISO 179/1eU 10 |
| 23°C | 70.3 | kJ/m² | ISO 179/1eU 11 |
| Notched Izod Impact | |||
| 23°C | 32 - 200 | J/m | ASTM D256 |
| 23°C | 3.0 - 25 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 83 - 1400 | J/m | ASTM D256 |
| 23°C | 28 - 97 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 8.93 - 25.1 | J | ASTM D3763 |
| 23°C | 2.00 - 9.19 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 560 - 1520 | N | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 206 - 223 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 198 - 223 | °C | ISO 75-2/B |
| 0.45 MPa | 215 | °C | ISO 75-2 12 |
| 1.8 MPa, not annealed | 187 - 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 188 - 218 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 182 - 211 | °C | ASTM D648 |
| 1.8 MPa | 205 | °C | ISO 75-2 13 |
| 8.0 MPa, not annealed | 55.0 - 191 | °C | ISO 75-2/C |
| Continuous Use Temperature | 89.0 - 200 | °C | ASTM D794 |
| Vicat Softening Temperature | |||
| -- | 198 - 217 | °C | ASTM D1525 |
| -- | 198 - 216 | °C | ISO 306 |
| Ball Indentation Temperature | 200 | °C | IEC 60598-1 |
| Melting Temperature | |||
| -- | 215 - 223 | °C | |
| -- | 220 - 222 | °C | DSC, ISO 11357-3, ISO 3146 |
| -- | 218 - 220 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | |||
| Flow | 9.5E-6 - 5.4E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-5 - 5.1E-5 | cm/cm/°C | ASTM E831 |
| Flow | 8.8E-6 - 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.7E-5 - 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral | 4.8E-5 - 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1300 - 1700 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | |||
| 23°C | 0.32 - 1.1 | W/m/K | ASTM C177 |
| 23°C | 0.21 - 0.46 | W/m/K | ISO 8302 |
| RTI Elec | 65.0 - 142 | °C | UL 746 |
| RTI Imp | 65.0 - 120 | °C | UL 746 |
| RTI | 65.0 - 142 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 3.5 - 2.5E+15 | ohms | ASTM D257 |
| -- | 5.0E+3 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.5 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+3 - 1.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 15 - 25 | kV/mm | ASTM D149 |
| 23°C | 19 - 80 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.00 - 4.35 | ASTM D150 | |
| 23°C | 3.47 - 4.04 | IEC 60250 | |
| 23°C | 3.65 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 0.010 - 0.021 | ASTM D150 | |
| 23°C | 5.0E-3 - 0.026 | IEC 60250 | |
| 1 MHz | 0.020 | IEC 60250 14 | |
| Arc Resistance | 117 - 133 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 490 - 500 | V | UL 746 |
| Comparative Tracking Index | |||
| -- | 394 - 600 | V | IEC 60112 |
| -- | 523 | IEC 60112 15 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 99 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 642 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 22 - 30 | % | ASTM D2863 |
| -- | 22 - 33 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.8 - 82.9 | °C | |
| Drying Time | 2.0 - 5.3 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Dew Point | -18.0 - -17.8 | °C | |
| Suggested Max Moisture | 0.095 - 0.20 | % | |
| Suggested Shot Size | 55 - 60 | % | |
| Suggested Max Regrind | 18 | % | |
| Hopper Temperature | 70.0 - 84.8 | °C | |
| Rear Temperature | 231 - 283 | °C | |
| Middle Temperature | 239 - 284 | °C | |
| Front Temperature | 244 - 283 | °C | |
| Nozzle Temperature | 234 - 294 | °C | |
| Processing (Melt) Temp | 249 - 292 | °C | |
| Mold Temperature | 58.1 - 100 | °C | |
| Injection Pressure | 6.89 - 106 | MPa | |
| Holding Pressure | 42.2 - 75.0 | MPa | |
| Back Pressure | 0.00 - 0.735 | MPa | |
| Screw Speed | 44 - 76 | rpm | |
| Cushion | 4.66 - 9.53 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 6 - Glass FiberThis information is provided for comparative purposes only. |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 13 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 14 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 15 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 530E3720010 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| TRANSMARE® 19HGF20-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| FHR EPS 55-7655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| Eltex® K3820-20 | INEOS Olefins & Polymers Europe | HDPE | Eltex® |
| Karina BLACK PVC COMPOUND 820-48/ 1-D-AC-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |