NYCOA Polyamide 6115 HS
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DP1nCW_NYCOA-Polyamide-6115-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NYCOA 6120 is a 15% glass fiber reinforced, impact modified, Nylon 6/12 that offers an excellent balance of mechanical properties. This grade features a higher degree of impact strength vs. traditional glass-filled Nylons. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 104 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 13 | % | ASTM D638 |
| Flexural Modulus 3 | 4000 | MPa | ASTM D790 |
| Flexural Strength 4 | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 310 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 217 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 227 - 238 | °C | |
| Middle Temperature | 238 - 249 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 65.6 - 76.7 | °C | |
| Injection Rate | Fast | ||
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tufel® II 94205 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| NEFTEKHIM PS 430 | Nizhnekamskneftekhim Inc. | PS (GPPS) | NEFTEKHIM PS |
| Boda BDF-H2852 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Karina BLACK PVC COMPOUND -E 650D48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 902-10/21-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |