Akulon® XP36-C1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DOB7DG_Akulon-XP36-C1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon®XP36-C1 is a polyamide 6 (nylon 6) material,. This product is available in Europe, and the processing method is: film extrusion. Akulon®The main features of the XP36-C1 are:
Akulon®The typical application fields of XP36-C1 are: movies |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Viscosity Number | 194 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ISO 8295 | ||
| With itself-dynamic, cast film | 1.0 | ISO 8295 | |
| With itself-static, cast film | 1.2 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus 1(50 µm, Cast Film) | 490 | MPa | Internal method |
| Tensile Stress - MD | ISO 527-3 | ||
| Yield, 50 µm, cast film | 33.0 | MPa | ISO 527-3 |
| 50 µm, cast film | 85.0 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Broken, 50 µm, cast film) | 340 | % | ISO 527-3 |
| Trouser Tear Resistance - MD (50 µm, Cast Film) | 23.0 | N/mm | ISO 6383-1 |
| Water Vapor Transmission Rate (23°C, 85% RH, 50 µm, cast film) | 35 | g/m²/24 hr | DIS 15106-1/-3 |
| Oxygen Transmission Rate 2 | DIS 15105-1/-2 | ||
| 0% RH : 23°C, 50.0 µm | 26 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| 85% RH : 23°C, 50.0 µm | 38 | cm³/m²/bar/24 hr | DIS 15105-1/-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity | |||
| -- | 1550 | J/kg/°C | |
| Average : 20 to 150°C | 2250 | J/kg/°C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (50.0 µm) 3 | 12.5 | J/cm | Internal method |
| RSV 4 | 3.00 | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (50.0 µm, Cast Film) | 83.0 | % | Internal method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (260°C) | 2740 | Pa·s | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Processing parameters for cast film test specimen: Extruder Temperature: 270°C Die Temperature: 270°C Chill Roll Temperature: 110°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 230 - 235 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 240 - 270 | °C | |
| Processing (Melt) Temp | 240 - 275 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 - 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Cast Film |
| 3 . | Cast Film |
| 4 . | Formic Acid, 1g/100 ml |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumiflex® QE QE533AEE | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| Borclear™ RF366MO | Borealis AG | PP, Unspecified | Borclear™ |
| Dynaflex™ G7650-1 (Natural) | PolyOne Corporation | TPE | Dynaflex™ |
| Kingfa PBT RG002 | Kingfa | PBT | Kingfa PBT |
| Karina IVORY PVC COMPOUND 851D35/ 1-B-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |