LightSpan® LS-6946

Category:	Silicone , Silicone
Manufacturer:	NuSil Technology
Trademark:	LightSpan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	DNZUvV_LightSpan-LS-6946.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
From LEDs to fiber optics, NuSil Technology's LightSpan™ brand product line delivers the most comprehensive line of refractive index matching adhesives, encapsulants and thermosets available. The benefits of silicone include the following: Thermal Stability Low Ionic Species Maintain Optical Clarity (90% minimum @ 400nm) Low Moisture Absorption (<0.4%) Optimization for UV Resistance Adjustable Cure Low Outgassing Low Shrinkage, <1% Low Modulus: Stress reduction for bonding materials with different coefficients of thermal expansion Gernal Purpose: Optical Adhesives and Elastomers Comments: Primed Lap Shear 510 psi, Youngs Modulus 425 psi

Message

From LEDs to fiber optics, NuSil Technology's LightSpan™ brand product line delivers the most comprehensive line of refractive index matching adhesives, encapsulants and thermosets available.

The benefits of silicone include the following:

Thermal Stability

Low Ionic Species

Maintain Optical Clarity (90% minimum @ 400nm)

Low Moisture Absorption (<0.4%)

Optimization for UV Resistance

Adjustable Cure

Low Outgassing

Low Shrinkage, <1%

Low Modulus: Stress reduction for bonding materials with different coefficients of thermal expansion

Gernal Purpose: Optical Adhesives and Elastomers

Comments: Primed Lap Shear 510 psi, Youngs Modulus 425 psi

General Information
Features	Good Thermal Stability Good UV Resistance Low Moisture Absorption Low Shrinkage Low to No Outgassing
Uses	Adhesives
Processing Method	Injection Molding

Thermal	Nominal Value	Unit
CLTE - Flow	3.6E-4	cm/cm/°C

Optical	Nominal Value
Refractive Index	1.460

Thermoset	Nominal Value	Unit
Thermoset Components
Part A	Mix Ratio by Weight: 1.0
Part B	Mix Ratio by Weight: 1.0

Uncured Properties	Nominal Value	Unit
Viscosity
-- ¹	35	Pa·s
-- ²	40	Pa·s
Curing Time (150°C)	0.50	hr
Pot Life	120	min

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	30
Lap Shear Strength	3.52	MPa
Tensile Modulus	2.93	MPa
Tensile Strength	4.65	MPa
Tensile Elongation at Break	280	%

Note Message
1 .	Part B
2 .	Part A

Resin Grade	Manufacturer	Category	Trademark
SuperLite® SL550800-100 (2.0mm)	Azdel, Inc.	PP, Unspecified	SuperLite®
Tarflen® SM-K22G3	Grupa Azoty S.A.	PTFE	Tarflen®
Honeywell PCTFE P5000HS	Honeywell	PCTFE	Honeywell PCTFE
Hostacom BB 1161 F M	LyondellBasell Industries	PP Copolymer	Hostacom
Karina LILAC 2563U -E TR-600N34/189-YT-AS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina