LAPEROS® E130i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | LAPEROS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DNBsI1_LAPEROS-E130i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Heat Resistance,High Flow, Glass fiber reinforced, Standard |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 1.00 mm | 0.54 | % | |
| Flow : 1.00 mm | 0.020 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 175 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 15000 | MPa | ISO 178 |
| Flexural Stress | 220 | MPa | ISO 178 |
| Flexural Strain | 2.3 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | VF2201/BK210P/BK205P |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 35 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 290 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 280 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.00 mm | 44 | kV/mm | |
| 3.00 mm | 24 | kV/mm | |
| Dielectric Constant | IEC 60250 | ||
| 1 kHz | 4.30 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 kHz | 0.020 | ||
| 1 MHz | 0.030 | ||
| Arc Resistance | 130 | sec | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1 mm; Inj. Pressure 60MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos PS HI 562E | Synthos S.A. | PS (HIPS) | Synthos PS |
| Yuyao PA 033ML20 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| Ajedium™ Films -- Thermoplastic Polyimide | Solvay Specialty Polymers | PI, TP | Ajedium™ Films |
| Daelim Po1y® LH-6070 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Plaskon MUF-2A | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |