ACCUTECH™ HP0334C10L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DLFciZ_ACCUTECH-HP0334C10L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0334C10L1 is a polypropylene homopolymer (PP Homopoly) product, and its filler is 10% calcium carbonate filler. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.4 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 35.0 | MPa | ASTM D638 |
| Fracture | 17.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 70 | % | ASTM D638 |
| Flexural Modulus | 1600 | MPa | ASTM D790 |
| Flexural Strength | 36.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 96.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 52.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® N 535 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| TABOREN PH 42 T 40 | SILON s.ro | PP Homopolymer | TABOREN |
| Moplen Q30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| VisiJet® CR-WT | 3D Systems | Unspecified | VisiJet® |
| LNP™ THERMOCOMP™ WX05502 compound | SABIC Innovative Plastics | TPEE | LNP™ THERMOCOMP™ |