Hylex® P1310G7FRMA
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DL2GC8_Hylex-P1310G7FRMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, 7% Glass Filled, Flame Retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 78.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 143 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 139 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R513H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Cellophane™ 320MS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Clariant Nylon 6/6 66G13-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Latiohm 66-10 H2 CNT CE/10 | LATI S.p.A. | Nylon 66 | Latiohm |
| Petrothene® NA362 | LyondellBasell Industries | LDPE | Petrothene® |